Effect of dendron structure on the luminescent and charge transporting properties of solution processed dendrimer-based OLEDs

The photophysical and charge transport properties of neat and blend films of fac -tris[2-phenylpyridinato- C 2 , N ]iridium( iii ) [Ir(ppy) 3 ]-cored light-emitting dendrimers and tris(4-carbazoyl-9-ylphenyl)amine (TCTA)-based hosts, with each combination having the same first generation dendrons we...

Full description

Saved in:
Bibliographic Details
Published in:Journal of materials chemistry. C, Materials for optical and electronic devices Materials for optical and electronic devices, 2021-11, Vol.9 (44), p.1633-1643
Main Authors: Gao, Mile, Mai, Van T. N, Jang, Junhyuk, Ranasinghe, Chandana Sampath Kumara, Chu, Ronan, Burn, Paul L, Gentle, Ian R, Pivrikas, Almantas, Shaw, Paul E
Format: Article
Language:English
Subjects:
Charge transport
Dendrimers
Emitters
Energy transfer
Evaporation
Hole mobility
Iridium
Photoluminescence
Quantum efficiency
Transport properties
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The photophysical and charge transport properties of neat and blend films of fac -tris[2-phenylpyridinato- C 2 , N ]iridium( iii ) [Ir(ppy) 3 ]-cored light-emitting dendrimers and tris(4-carbazoyl-9-ylphenyl)amine (TCTA)-based hosts, with each combination having the same first generation dendrons were measured and compared. The first generation dendrons were composed of bis(fluorenyl)carbazolyl with n -propyl surface groups, or biphenyl with 2-ethylhexyloxy or t -butyl surface groups. Dendronisation of the emitter and host was found to decrease the energy transfer efficiency from the host to the guest relative to an evaporated Ir(ppy) 3 :TCTA blend film, with the blend composed of materials with biphenyl dendrons and t -butyl surface groups having the largest decrease. The hole mobilities of the solution processed neat and blend layers were found to be 1-2 orders of magnitude lower than those of the equivalent evaporated films. The blend film containing the host and dendrimer with first generation biphenyl dendrons and 2-ethylhexyloxy surface groups had the highest photoluminescence quantum yield (PLQY), comparable to evaporated Ir(ppy) 3 :TCTA-based films but the lowest hole mobility ( 10 −8 cm 2 V −1 s −1 ). In contrast, the blend with the dendrimers composed of the bis(fluorenyl)carbazolyl dendrons with n -propyl surface groups had a low PLQY but higher hole mobility. It was found for the combinations of these solution processable materials that the hole mobility of the blend film was the limiting factor in OLED performance. Devices containing an emissive layer of the materials with the bis(fluorenyl)carbazolyl dendrons with n -propyl surface groups (11 mole percent of the emitter) had a PLQY of 40.8% but the highest external quantum efficiency of 10.0 ± 0.4%, reaching a maximum luminance of almost 10 000 cd m −2 . The energy transfer, PLQY, charge mobility, and OLED performance of blend films of first generation Ir(ppy) 3 -cored light-emitting dendrimers and dendrimeric TCTA-based hosts are found to be dependent on the dendrons and surface groups used.
ISSN:2050-7526
2050-7534
DOI:10.1039/d1tc03949k