The microstructure and property of Al–Si alloy and Al–Mn alloy bimetal prepared by continuous casting
The Al–10%Si alloy and Al–1%Mn alloy bimetal slabs are prepared by continuous casting. The microstructures around the interface are investigated, chemical composition distributions across the interface are detected, and tensile strengths are evaluated at the top, center and bottom regions of the bim...
Saved in:
Published in: | Materials letters 2012-01, Vol.67 (1), p.21-23 |
---|---|
Main Authors: | , , , , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | The Al–10%Si alloy and Al–1%Mn alloy bimetal slabs are prepared by continuous casting. The microstructures around the interface are investigated, chemical composition distributions across the interface are detected, and tensile strengths are evaluated at the top, center and bottom regions of the bimetal slab. The results show that the Al–1%Mn alloy serves as a substrate of heterogeneous nucleation of Al–10%Si alloy at the bimetal interface. The metallurgical bonding is excellent without any discontinuities along the interface due to the diffusions of Si and Mn elements. The thickness of diffusion layers is about 40
μm on average. The tensile strengths of the top, center and bottom regions of the bimetal slab tend to be uniform.
► The bimetal slab consisting of Al–10%Si alloy and Al–1%Mn is produced by cast. ► Metallurgical bond occurs during the solidification due to diffusions of Si and Mn. ► The thickness of the diffusion layer of the bimetal slab is about 40
μm. ► Al–1%Mn alloy serves as the substrate for heterogeneous nucleation of Al–10%Si alloy. |
---|---|