Co–Pt alloy nanoparticles produced using a template of nanoparticle array
A monolayer of Co–Pt alloy nanoparticles in the nanometer-size regime was fabricated using a nanotemplate approach. 1.7-nm-thick Co46Pt54 film was deposited onto a preexisting array of Ni seed particles embedded in a polyimide film. During subsequent annealing, the deposited Co46Pt54 film coalesced...
Saved in:
Published in: | Journal of colloid and interface science 2006-11, Vol.303 (1), p.131-136 |
---|---|
Main Authors: | , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | A monolayer of Co–Pt alloy nanoparticles in the nanometer-size regime was fabricated using a nanotemplate approach. 1.7-nm-thick Co46Pt54 film was deposited onto a preexisting array of Ni seed particles embedded in a polyimide film. During subsequent annealing, the deposited Co46Pt54 film coalesced onto the seed particles to produce a monolayer of Co–Pt alloy particles. Deposition and annealing were repeated to increase both average particle size and volume fraction of the alloy particles. It was also shown that the annealing temperature was critical in controlling the particle size distribution and the final composition of the nanoparticles. This method of forming a single layer of vertically aligned nanoparticles can be easily extended to a large area as well as to produce a different combination of alloy particles on a polymer film. |
---|---|
ISSN: | 0021-9797 1095-7103 |
DOI: | 10.1016/j.jcis.2006.07.018 |