Tarnish protection of silver by octadecanethiol self-assembled monolayers prepared in aqueous micellar solution

Silver will tarnish when it is exposed to the sulfur polluted atmosphere. Self-assembled monolayers are an efficient, invisible and protective film against tarnishing. SAMs prepared by the adsorption of octadecanethiol onto silver in aqueous micellar solution are explored. The silver was first degre...

Full description

Saved in:
Bibliographic Details
Published in:Surface & coatings technology 2009-01, Vol.203 (8), p.1034-1044
Main Authors: Liang, Chenghao, Yang, Changjiang, Huang, Naibao
Format: Article
Language:English
Subjects:
Applied sciences
Atmospheric corrosion
Coating
Corrosion
Corrosion environments
Cross-disciplinary physics: materials science
rheology
Exact sciences and technology
Materials science
Metals. Metallurgy
Physics
Production techniques
SAMs
Silver
Surface treatment
Surface treatments
Tarnish
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Silver will tarnish when it is exposed to the sulfur polluted atmosphere. Self-assembled monolayers are an efficient, invisible and protective film against tarnishing. SAMs prepared by the adsorption of octadecanethiol onto silver in aqueous micellar solution are explored. The silver was first degreased by acetone in an ultra-sonicate bath, followed by activation in 10% sulphuric acid solution, then, immersed in aqueous micellar solution with 0.15 mol/L octadecanethiol and 40 g/L Cetane trimethyl ammonium bromide (CTAB), Triton X-100 (TX-100), Polyoxyethylene lauryl ether (PLE) or Pluronic PE6400 during 5 min at 60 °C. The film was characterized by contact angles, FT-IR, XPS and AFM. The film was totally composed of octadecanethiol and was influenced by the surfactant in the thickness and tilt angle. The anti-tarnishing ability of the film on the silver was evaluated by electrochemical measurements in 0.5 mol/L NaCl solution containing 10 mmol/L Na 2S. The protection efficiency reached 91.9% The electro-oxidation reaction process was reduced substantially in 0.5 mol/L NaOH solution. EIS data proved that the inhibition of the monolayers was marked and the coverage of the film was more than 94.5%. The color, gloss and reflectance of silver with SAMs were almost similar to the bare silver. It was found that after 48 h accelerated tarnishing test, the protection of the thiol film remained efficient. The film controlled markedly the transfer of ion to the surface and the sulfuration rate of silver was reduced substantially.
ISSN:0257-8972
1879-3347
DOI:10.1016/j.surfcoat.2008.09.034