The Surface Deterioration of Prefabricated Zirconia Crowns on Exposure to Acidulated Phosphate Fluoride Gel: An In Vitro Study

Introduction Zirconia is a widely used restorative material in dentistry due to its superior aesthetic and mechanical properties. The oral cavity is a complex ecosystem with various components, which affect the teeth, as well as artificial restorative materials. Various personal and professional int...

Full description

Saved in:
Bibliographic Details
Published in:Curēus (Palo Alto, CA) CA), 2024-08, Vol.16 (8), p.e66371
Main Authors: Makwana, Sanidhya L, Vaishnav, Kalpesh, Joshi, Ravi, Patel, Tulsi H, Vora, Neil N, Sachde, Nishit H, Vala, Keyur A, Raval, Zalak, Yohannan, Jinsa A, Joshi, Vidhi J
Format: Article
Language:English
Citations: Items that this one cites
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Introduction Zirconia is a widely used restorative material in dentistry due to its superior aesthetic and mechanical properties. The oral cavity is a complex ecosystem with various components, which affect the teeth, as well as artificial restorative materials. Various personal and professional interventions carried out can severely affect the properties of restorative materials, thus altering the longevity of the prosthesis; 1.23% acidulated phosphate fluoride (APF) gel is one such professionally applied topical fluoride agent used to prevent caries. The interaction of this APF gel with highly aesthetic restorative material such as zirconia crowns is unknown. Objective The objective of this study is the evaluation of the surface deterioration of prefabricated zirconia crowns on exposure to deionised water and 1.23% acidulated phosphate fluoride (APF) gel with field emission scanning electron microscope (FE-SEM) and mass loss analysis. Material and method Sixty prefabricated paediatric zirconia crowns were taken, 10 samples were immersed in deionised water, 40 samples were immersed in 1.23% APF gel and 10 samples were used as control. Surface morphology and mass loss analysis were carried out at time intervals of four minutes, 24 hours, 48 hours and 72 hours using FE-SEM and digital weighing machine. Results No visual change was observed in the samples immersed in deionised water at the time interval of 72 hours. There was a marked visual change in samples immersed in 1.23% APF gel at the time interval of four minutes to 72 hours; this change involved a loss of gloss to the appearance of chalkiness. FE-SEM analysis for the control group and samples immersed in deionised water showed a smooth, continuous, undisrupted top layer, while samples immersed in 1.23% APF gel showed changes ranging from surface etching, to pinhole porosities, to crack formation and disruption of the surface depending upon the exposure time. Conclusions On the immersion of zirconia crowns in an aqueous acidic medium of 1.23% APF gel, the crowns showed flaws, imperfections and uneven superficial layers. It has been observed that surface grains are disrupted and micropores have been formed. This degraded superficial surface when undergoes cyclic mechanical loading can accelerate the ageing phenomenon of zirconia. Mechanical forces along with a dynamic electrochemical environment can degrade the material properties of zirconia.Introduction Zirconia is a widely used restorative material
ISSN:2168-8184
2168-8184
DOI:10.7759/cureus.66371