Cure shrinkage characterization and modeling of a polyester resin containing low profile additives

Resin Transfer Moulding (RTM) has great potential as an efficient and economical process for fabricating large and complicated composite structural components. The low capital investment cost required and process versatility in component integration and assembly make RTM very attractive for high vol...

Full description

Saved in:
Bibliographic Details
Published in:Composites. Part A, Applied science and manufacturing Applied science and manufacturing, 2007-03, Vol.38 (3), p.994-1009
Main Authors: Haider, Mohsan, Hubert, Pascal, Lessard, Larry
Format: Article
Language:English
Subjects:
Applied sciences
B. Curing-chemical shrinkage
B. Rheological properties
Composites
D. Thermal analysis
E. Resin transfer moulding (RTM)
Exact sciences and technology
Forms of application and semi-finished materials
Polymer industry, paints, wood
Technology of polymers
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Resin Transfer Moulding (RTM) has great potential as an efficient and economical process for fabricating large and complicated composite structural components. The low capital investment cost required and process versatility in component integration and assembly make RTM very attractive for high volume automotive applications. One of the challenges facing the automotive field is the resulting surface finish of manufactured components. The shrinkage associated with the curing of thermoset resins contributes to the poor surface quality. Low profile additives (LPA) are added to the resin to compensate for the cure shrinkage; however their effects on the thermal, rheological and morphological properties of polyester resins are not well understood. In this paper, the effect of LPA on cure kinetics, cure shrinkage and viscosity of a polyester resin is studied through differential scanning calorimetry (DSC) and special rheological techniques. Models are developed to predict cure shrinkage, LPA expansion, cure kinetics and viscosity variations of the resin as a function of processing temperature. Finally, morphological changes in the resin with and without LPA, during isothermal cure, are studied with hot stage optical microscopy. The results show that the LPA content in the range tested had no significant effect on the cure kinetics. However, higher LPA content reduced cure rate and cure shrinkage. A minimum of 10% LPA was required to compensate for cure shrinkage. Shrinkage behavior of all formulations was similar until a degree-of-cure of 0.5. However, resin formulations with higher LPA content showed expansion at later stages during curing.
ISSN:1359-835X
1878-5840
DOI:10.1016/j.compositesa.2006.06.020