A study on the deactivation of an IrO2–Ta2O5 coated titanium anode

The deactivation of an IrO2-Ta2O5 coated titanium anode was studied during an accelerated life test at 2 Acm-2 2 in 1 mol dm-3 H2SO4 solution using CV, EIS, SEM and EDX. The changes of voltammetric charge, double layer capacitance, oxide film resistance and charge transfer resistance of oxygen evolu...

Full description

Saved in:
Bibliographic Details
Published in:Corrosion science 2003-12, Vol.45 (12), p.2729-2740
Main Authors: Xu, L.K, Scantlebury, J.D
Format: Article
Language:English
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The deactivation of an IrO2-Ta2O5 coated titanium anode was studied during an accelerated life test at 2 Acm-2 2 in 1 mol dm-3 H2SO4 solution using CV, EIS, SEM and EDX. The changes of voltammetric charge, double layer capacitance, oxide film resistance and charge transfer resistance of oxygen evolution with time during the electrolysis were monitored. The morphology and surface composition of the oxide anode before and after electrolysis test were analysed. A comprehensive process of deactivation of the oxide anode was proposed based on the test results and analysis.
ISSN:0010-938X
DOI:10.1016/S0010-938X(03)00108-2