Sensitive and Selective NO2 Sensing Based on Alkyl- and Alkylthio-Thiophene Polymer Conductance and Conductance Ratio Changes from Differential Chemical Doping

NO2-responsive polymer-based organic field-effect transistors (OFETs) are described, and room-temperature detection with high sensitivity entirely from the semiconductor was achieved. Two thiophene polymers, poly­(bisdodecylquaterthiophene) and poly­(bisdodecylthioquaterthiophene) (PQT12 and PQTS12,...

Full description

Saved in:
Bibliographic Details
Published in:ACS applied materials & interfaces 2017-06, Vol.9 (24), p.20501-20507
Main Authors: Li, Hui, Dailey, Jennifer, Kale, Tejaswini, Besar, Kalpana, Koehler, Kirsten, Katz, Howard E
Format: Article
Language:English
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:NO2-responsive polymer-based organic field-effect transistors (OFETs) are described, and room-temperature detection with high sensitivity entirely from the semiconductor was achieved. Two thiophene polymers, poly­(bisdodecylquaterthiophene) and poly­(bisdodecylthioquaterthiophene) (PQT12 and PQTS12, respectively), were used as active layers to detect a concentration at least as low as 1 ppm of NO2. The proportional on-current change of OFETs using these polymers reached over 400% for PQTS12, which is among the highest sensitivities reported for a NO2-responsive device based on an organic semiconducting film. From measurements of cyclic voltammetry and the electronic characteristics, we found that the introduction of sulfurs into the side chains induces traps in films of the PQTS12 and also decreases domain sizes, both of which could contribute to the higher sensitivity of PQTS12 to NO2 gas compared with PQT12. The ratio of responses of PQTS12 and PQT12 is higher for exposures to lower concentrations, making this parameter a means of distinguishing responses to low concentrations for extended times from exposures to high concentrations from shorter times. The responses to nonoxidizing vapors were much lower, indicating good selectivity to NO2 of two polymers. This work demonstrates the capability of increasing selectivity and calibration of OFET sensors by modulating redox and aggregation properties of polymer semiconductors.
ISSN:1944-8244
1944-8252
DOI:10.1021/acsami.7b02721