Fabrication and Properties of Porous Carbon Preforms for Making Reaction Formed SiC
This paper describes a proper low cost way to fabricate defects free porous carbon preforms with interconnect pore structure for making reaction formed SiC (RFSC). Taking charcoal , poplar powder, camphene and polymer dispersant together, making slurries by milling under 55 °C for several hours, con...
Saved in:
Published in: | Key Engineering Materials 2016-07, Vol.697, p.169-172 |
---|---|
Main Authors: | , , , , , , , |
Format: | Article |
Language: | eng |
Subjects: | |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | This paper describes a proper low cost way to fabricate defects free porous carbon preforms with interconnect pore structure for making reaction formed SiC (RFSC). Taking charcoal , poplar powder, camphene and polymer dispersant together, making slurries by milling under 55 °C for several hours, controlling the content of charcoal and poplar powder, after casting, sublimating and carbonizing, the porous carbon performs with a series density (0.66 g/cm3-0.78 g/cm3) and porosity (62.9 vol.%-68.6 vol.%) were prepared; through the Si infiltrating process under a vacuum condition (~5.0 Pa) at 1500°C for about 0.5 hour, the RFSCs with fine mechanic performance were fabricated, one RFSC sample has the density, Weibull modulus, and the max three points flexural strength is 2.91 g/cm3, 9.5 and 505.0 MPa respectively. |
---|---|
ISSN: | 1013-9826 1662-9795 1662-9795 |