Mechanical Properties and Microstructure of Thin-Walled Al-Cu Alloy Casting
This study aimed to investigate the tensile properties and microstructure of Al-Cu alloy casting with a dimension of ∅500 mm × 700 mm and a 5mm-thick wall at room temperature and 200°C. The results indicated that the strength and elongation of Al-Cu alloy casting at room temperature were excellent,...
Saved in:
Published in: | Strength of materials 2022-03, Vol.54 (2), p.302-308 |
---|---|
Main Authors: | , , , , , , , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | This study aimed to investigate the tensile properties and microstructure of Al-Cu alloy casting with a dimension of ∅500 mm × 700 mm and a 5mm-thick wall at room temperature and 200°C. The results indicated that the strength and elongation of Al-Cu alloy casting at room temperature were excellent, exceeding 425 MPa and 8%, respectively. Such a good performance was attributed to the tiny equiaxed grains. However, the occurrence of acicular θ phase distributed around the α-Al matrix grains was disadvantageous to strength and especially to elongation. Moreover, no dynamic recrystallization was observed in the tensile tests at 200°C. Besides, numerous dimples were found in the fracture morphology, which were beneficial to the elongation. |
---|---|
ISSN: | 0039-2316 1573-9325 |
DOI: | 10.1007/s11223-022-00406-2 |