Self-healing performance and corrosion resistance of novel CeO2-sealed MAO film on aluminum alloy
The self-healing performance with the improved corrosion resistance of novel CeO2-sealed micro-arc oxide (MAO) film on Al alloy was studied in this work for the first time. There are three steps involved, including: (1) Preparing porous film by performing MAO treatment on Al alloy with the average t...
Saved in:
Published in: | Surface & coatings technology 2021-07, Vol.417, p.127208, Article 127208 |
---|---|
Main Authors: | , , , , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | The self-healing performance with the improved corrosion resistance of novel CeO2-sealed micro-arc oxide (MAO) film on Al alloy was studied in this work for the first time. There are three steps involved, including: (1) Preparing porous film by performing MAO treatment on Al alloy with the average thickness of ~15 μm; (2) loading corrosion inhibitor by soaking MAO sample in Ce(NO3)3 solution to fulfill micropores-sealing process; (3) evaluating the self-healing ability of the sealed MAO film in acidic, alkaline and neutral solutions by scratch tests. The experimental results indicated that the corrosion inhibitor was characterized to be CeO2 which can locally fill the micropores to seal the MAO film. The optimized CeO2-sealed MAO film owned the lower porosity and the improved the corrosion resistance, which can be testified from the corrosion current density (Icorr) decreased by 2 orders of magnitude compared with the MAO film. Furthermore, the micropores in the MAO film acted as microcontainers to hold corrosion inhibitor to make CeO2-sealed MAO film showed self-healing ability. In the acidic environment (pH = 2 (8 mL/L H2SO4 + 20 mL/L H2O2)), the novel CeO2-sealed film exhibited positive self-healing effect morphologically with improved corrosion test result, and the underlying self-healing mechanism was discussed in detail.
•Ce(NO3)3 solution is to induce the creation of corrosion inhibitor into MAO film.•The sealing behavior of the CeO2 corrosion inhibitor to MAO film is revealed.•The corrosion resistance of CeO2-sealed MAO film is improved significantly.•CeO2-sealed MAO film presents self-healing effect in acidic environment.•Self-healing mechanism of CeO2-sealed film in acidic environment is clarified. |
---|---|