From thin to extra-thick adhesive layer thicknesses: Fracture of bonded joints under mode I loading conditions

•The mode I fracture toughness presents similar values for thicknesses of 0.4–2.6 mm.•The fracture toughness increases by 63% for 4.1 mm.•The fracture toughness decreases about 10% for the 10.1 mm, in relation with 4.1 mm.•The crack path, failure surfaces and stress ahead of the crack tip explain th...

Full description

Saved in:
Bibliographic Details
Published in:Engineering fracture mechanics 2019-09, Vol.218, p.106607, Article 106607
Main Authors: Lopes Fernandes, Romina, Teixeira de Freitas, Sofia, Budzik, Michal K., Poulis, Johannes A., Benedictus, Rinze
Format: Article
Language:English
Subjects:
Adhesion tests
Adhesive bonding
Adhesive joints
Beam theory (structures)
Bonded joints
Cantilever beams
Crack tips
Epoxy adhesives
Extra-thick bond lines
Failure surface
Fracture process zone
Fracture toughness
Mode I
Strain energy release rate
Stress distribution
Thickness
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:•The mode I fracture toughness presents similar values for thicknesses of 0.4–2.6 mm.•The fracture toughness increases by 63% for 4.1 mm.•The fracture toughness decreases about 10% for the 10.1 mm, in relation with 4.1 mm.•The crack path, failure surfaces and stress ahead of the crack tip explain the trend. The fracture behaviour of joints bonded with a structural epoxy adhesive and bond line thicknesses of 0.1–4.5 mm has been studied. However, limited research is found on similar joints with thicker bond lines, which are relevant for maritime applications. Therefore, the effect of the adhesive bond line thickness, varying from 0.4 to 10.1 mm, on the mode I fracture behaviour of steel to steel joints bonded with a structural epoxy adhesive was investigated in this study. An experimental test campaign of double-cantilever beam (DCB) specimens was carried out in laboratory conditions. Five bond line thicknesses were studied: 0.4, 1.1, 2.6, 4.1 and 10.1 mm. Analytical predictions of the experimental load-displacement curves were performed based on the Simple Beam Theory (SBT), the Compliance Calibration Method (CCM) and the Penado-Kanninen (P-K) model. The P-K model was used to determine the mode I strain energy release rate (SERR). The average mode I SERR, GIav., presented similar values for the specimens with adhesive bond line thicknesses of 0.4, 1.1 and 2.6 mm (GI av.=0.71, 0.61, 0.63 N/mm, respectively). However, it increased by approximately 63% for 4.1 mm (GI av.=1.16 N/mm) and decreased by about 10% (in comparison with 4.1 mm) for the 10.1 mm (GI av.=1.04 N/mm). The trend of the GIav. in relation to the bond line thickness is explained by the combination of three factors: the crack path location, the failure surfaces features and the stress field ahead of the crack tip.
ISSN:0013-7944
1873-7315
DOI:10.1016/j.engfracmech.2019.106607