Dielectric and piezoelectric properties of PbTi 0.8−x Se0.2Sm x O3 nanoceramics prepared by high energy ball milling
Incorporation of Se and Sm were done based on the stoichiometric formula PbTi0.8−xSe0.2SmxO3 (PTSeS). TG characterization of green powder revealed the completion of solid state reaction at temperature 450 °C. XRD of modified PTSeS powders milled for 10 h was found most suitable as it gives pure sing...
Saved in:
Published in: | Applied physics. A, Materials science & processing Materials science & processing, 2019-01, Vol.125 (3), p.1-6 |
---|---|
Main Authors: | , , |
Format: | Article |
Language: | English |
Subjects: | |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Incorporation of Se and Sm were done based on the stoichiometric formula PbTi0.8−xSe0.2SmxO3 (PTSeS). TG characterization of green powder revealed the completion of solid state reaction at temperature 450 °C. XRD of modified PTSeS powders milled for 10 h was found most suitable as it gives pure single phase tetragonal structure. Dielectric constant was found as 2700 at curie temperature of 470 °C in the case of 5 wt percent of Sm in PTSeS. Piezoelectric coefficient was found as 230 × 10 − 12 C/N at 35 Kv/cm of poling field. The results obtained were comparable and even better than so far reported in similar kind of materials. |
---|---|
ISSN: | 0947-8396 1432-0630 |
DOI: | 10.1007/s00339-019-2425-z |