Crack-particle interactions during intergranular stress corrosion of AA5083 as observed by cross-section transmission electron microscopy
Studies of intergranular stress corrosion cracks growing in AA5083 aged to contain β-phase (Al 3Mg 2) particles at the grain boundary are reported. These studies have shown that for tests in a NaCl + K 2CrO 4 solution that β-phase particles are converted to Al 2O 3 particles and that the crack propa...
Saved in:
Published in: | Scripta materialia 2004-05, Vol.50 (10), p.1355-1359 |
---|---|
Main Authors: | , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Studies of intergranular stress corrosion cracks growing in AA5083 aged to contain β-phase (Al
3Mg
2) particles at the grain boundary are reported. These studies have shown that for tests in a NaCl
+
K
2CrO
4 solution that β-phase particles are converted to Al
2O
3 particles and that the crack propagates through or around them. |
---|---|
ISSN: | 1359-6462 1872-8456 |
DOI: | 10.1016/j.scriptamat.2004.01.038 |