Mechanical properties and energy absorption capability of thin-walled square columns of silica/epoxy nanocomposite

•Crashworthy capability of composite thin-walled square columns is investigated.•Effect of nanosilica content, particle size and various combinations of epoxy/silica.•Young’s modulus, yield strength and specific energy absorption were investigated.•Initiation of axial cracks at an early stage of the...

Full description

Saved in:
Bibliographic Details
Published in:Construction & building materials 2015-03, Vol.78, p.362-368
Main Authors: Shariati, Mahmoud, Farzi, Gholamali, Dadrasi, Ali
Format: Article
Language:English
Subjects:
Analysis
Energy absorption
Epoxy resins
Mechanical properties
Particle size
Silica
Silica nanoparticles
Thin-walled structures
Weight percent
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:•Crashworthy capability of composite thin-walled square columns is investigated.•Effect of nanosilica content, particle size and various combinations of epoxy/silica.•Young’s modulus, yield strength and specific energy absorption were investigated.•Initiation of axial cracks at an early stage of the loading was observed.•Shorter specimens have higher crashworthy capability in the same combination. In this paper, the effect of adding silica nanoparticle to epoxy, silica weight percent, particle size and various combinations of epoxy/silica on Young’s modulus, yield strength and energy absorption capability of thin-walled square columns was investigated. Two different sizes of silica nanoparticles, nominally 17nm and 65nm in diameter, were used. Nanosilica particles were dispersed almost homogeneously in the epoxy resin from 1.5wt.% to 6wt.% in three series of composites. First and second series were composites reinforced with 17nm and 65nm particle size, respectively and third series were composites reinforced with combination of both particle sizes. All specimens were tested under quasi-static loading using a servohydraulic Instron machine. A scanning electron microscopy (SEM) was used for fracture surface studies. The results showed that when silica weight percent was increased, the Young’s modulus increased, yield strength remained constant and energy absorption capability of columns decreased, and specimens collapsed under unstable and dangerous mode. It was observed that the reason for this type of collapse was initiation of axial cracks at an early stage of the loading and propagation along the specimen height. Energy absorption capability for columns with height of 60mm and 90mm was also investigated and results showed that this parameter for shorter specimens was higher in the same combination of a nanocomposite. Moreover, the effect of particle size on Young’s modulus, yield strength and energy absorption capability was not considerable. Using both particles in a combination did not show any important synergy effect. And finally, fracture surfaces of the specimens showed that surface roughness was increased by increasing the silica nanoparticles.
ISSN:0950-0618
1879-0526
DOI:10.1016/j.conbuildmat.2015.01.031