Alkali-activated binder containing wastes: a study with rice husk ash and red ceramic
Abstract In addition to several positive aspects in technical properties, geopolymeric binders have considerable advantages in the environmental point of view, with lower energy consumption and lower CO2 emission. In this study, it was conducted an overview about the utilized materials by some Brazi...
Saved in:
| Published in: | Cerâmica 2017-03, Vol.63 (365), p.44-51 |
|---|---|
| Main Authors: | , , , |
| Format: | Magazinearticle |
| Language: | eng |
| Subjects: | |
| Online Access: | Get full text |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Abstract In addition to several positive aspects in technical properties, geopolymeric binders have considerable advantages in the environmental point of view, with lower energy consumption and lower CO2 emission. In this study, it was conducted an overview about the utilized materials by some Brazilian researchers in geopolymers production, and also an experiment employing two types of wastes (red ceramic waste and rice husk ash). The compressive strength of the resulting material developed very fast, reaching a value of 11 MPa after one day. The microstructure was evaluated by scanning electron microscopy, revealing a compact microstructure and the presence of starting materials from the red ceramic waste that not completely reacted. The results indicated the feasibility of producing geopolymeric material without using commercial sodium silicate and cured at room temperature, showing an option for building materials production with lower environmental impacts.
Resumo Além de vários aspectos positivos nas propriedades técnicas, aglomerantes geopoliméricos têm consideráveis vantagens do ponto de vista ambiental, com menor consumo de energia e menor emissão de CO2. Neste estudo, conduziu-se uma revisão sobre os materiais empregados na produção de geopolímeros por alguns pesquisadores brasileiros, e também um experimento empregando-se dois tipos de resíduos (resíduos de cerâmica vermelha e cinza de casca de arroz). A resistência à compressão do material resultante desenvolveu-se muito rapidamente, alcançando valor de 11 MPa após 1 dia. A microestrutura foi analisada por microscopia eletrônica de varredura, revelando uma microestrutura compacta e a presença de materiais precursores do resíduo de cerâmica vermelha que não reagiram completamente. Os resultados indicaram a viabilidade de se produzir material geopolimérico sem usar o silicato de sódio comercial e curado em temperatura ambiente, apresentando uma opção para a produção de materiais de construção com menores impactos ambientais. |
|---|---|
| ISSN: | 0366-6913 1678-4553 0366-6913 |