First Performance Results of Ce:GAGG Scintillation Crystals With Silicon Photomultipliers

A new single-crystal Cerium doped Gd 3 Al 2 Ga 3 O 123 Al 2 Ga 3 O 12 (GAGG) scintillation crystal with high luminosity, high density and relatively fast decay time has successfully been grown. We report on the first performance results of the new GAGG scintillation crystal read out with silicon pho...

Full description

Saved in:

Bibliographic Details
Published in:	IEEE transactions on nuclear science 2013-04, Vol.60 (2), p.988-992
Main Authors:	Jung Yeol Yeom, Yamamoto, S., Derenzo, S. E., Spanoudaki, V. C., Kamada, K., Endo, T., Levin, C. S.
Format:	Article
Language:	eng
Subjects:	Ce:GAGG Crystals Energy resolution gamma-ray spectroscopy PET Photomultipliers Photonics Positron emission tomography scintillators Silicon silicon photomultipliers SPECT Timing
Online Access:	Get full text
Tags:	Add Tag No Tags, Be the first to tag this record!

Description
Summary:	A new single-crystal Cerium doped Gd 3 Al 2 Ga 3 O 123 Al 2 Ga 3 O 12 (GAGG) scintillation crystal with high luminosity, high density and relatively fast decay time has successfully been grown. We report on the first performance results of the new GAGG scintillation crystal read out with silicon photomultipliers (SiPM) from Hamamatsu (MPPC) and FBK. The best energy resolution (511 keV peak of Ge-68) of 7.9% was attained with GAGG coupled to MPPC and 9.0% with the FBK SiPM after correcting for non-linearity. On the other hand, the best coincidence resolving time (FWHM) of polished 3 × 3 × 5 mm 3 and 3 × 3 × 20mm 3 crystals were 464 ±12 ps and 577 ±22 ps for GAGG crystals compared to 179 ±8 ps and 214 ±6 ps for LYSO crystals respectively with MPPCs. The rise time of GAGG was measured to be 200 ps (75%) and 6 ns (25%) while the decay time was 140 ns (92%), 500 ns (7.7%) 6000 ns (0.3%).
ISSN:	0018-9499 1558-1578