Investigation of the Mechanism Resulting in low Resistance Ag Thick-Film Contact to Si Solar Cells in the Context of Emitter Doping Density and Contact Firing for Current-Generation Ag Paste

Screen-printed thick-film Ag metallization has become highly successful in crystalline Si (c-Si) photovoltaics. However, a complete understanding of the mechanism resulting in low resistance contact is still lacking. In order to shed light on this mechanism for current-generation Ag paste, Si solar...

Full description

Saved in:
Bibliographic Details
Published in:IEEE journal of photovoltaics 2014-01, Vol.4 (1), p.134-141
Main Authors: Cooper, Ian B., Tate, Keith, Renshaw, John S., Carroll, Alan F., Mikeska, Kurt R., Reedy, Robert C., Rohatgi, Ajeet
Format: Article
Language:English
Subjects:
Contacts
Glass
Junctions
metallization
p-n junctions
Photovoltaic cells
Resistance
Silicon
silver
Temperature
Temperature measurement
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Screen-printed thick-film Ag metallization has become highly successful in crystalline Si (c-Si) photovoltaics. However, a complete understanding of the mechanism resulting in low resistance contact is still lacking. In order to shed light on this mechanism for current-generation Ag paste, Si solar cells were fabricated using a range of emitter doping densities and contact firing conditions. Low resistance contact was found to vary as a function of emitter surface P concentration ( [P surface ]) and peak firing temperature. Scanning electron microscope (SEM) analysis revealed thin interfacial glass films (IGF) under the bulk Ag gridline. SEM analysis also showed increasing Ag crystallite density as both emitter [P surface ] and peak firing temperature increased. Two mechanisms are proposed in forming low resistance contact to highly doped emitters: 1) formation of ultrathin IGF and/or nano-Ag colloids at low firing temperature, and 2) formation of Ag crystallites at high firing temperature. However, on lightly doped emitters, low resistance contact was achieved only at higher firing temperatures, concomitant with increasing Ag crystallite density, and suggests that thin IGF decorated with nano-Ag colloids may not be sufficient for low resistance contact to lightly doped emitters.
ISSN:2156-3381
2156-3403
DOI:10.1109/JPHOTOV.2013.2285621