Strongly anisotropic field emission from highly aligned carbon nanotube films

The field electron emission properties of carbon nanotube (CNT) films composed of densely packed and highly aligned CNTs were investigated. The CNT films were produced by a continuous film casting process and are spooled into long lengths with the CNTs aligned lengthwise in the film. The anisotropic...

Full description

Saved in:
Bibliographic Details
Published in:Journal of applied physics 2021-03, Vol.129 (12)
Main Authors: Fairchild, S. B., de Assis, Thiago A., Park, J. H., Cahay, M., Bulmer, J., Tsentalovich, D. E., Ang, Yee Sin, Ang, L. K., Ludwick, J., Back, T. C., Pasquali, M.
Format: Article
Language:English
Subjects:
Alignment
Applied physics
Carbon nanotubes
Configuration management
Continuous casting
Damage
Electric fields
Electron emission
Experiments
Field emission
Microstructure
Minimal surfaces
Morphology
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The field electron emission properties of carbon nanotube (CNT) films composed of densely packed and highly aligned CNTs were investigated. The CNT films were produced by a continuous film casting process and are spooled into long lengths with the CNTs aligned lengthwise in the film. The anisotropic nature of the CNT film morphology was confirmed by performing specific conductivity measurements in directions both parallel and perpendicular to the aligned CNT microstructure. Field emission experiments were performed on 5 and 10 mm wide films that were mechanically cut into small samples and then vertically mounted so that the emission occurred from the film edge. The films were mounted with the aligned CNT microstructure oriented either parallel or perpendicular to the direction of the applied electric field. The highest emission currents were produced by films mounted in the parallel alignment configuration. Additional experiments were performed on films that were folded, which eliminated surface irregularities at the film edge due to the cutting process. SEM imaging performed at the ridge of the folded film before and after field emission (FE) experiments showed that films mounted in the parallel alignment configuration had minimal surface damage after FE, while films mounted in the perpendicular alignment configuration showed substantial damage. The effective emission area and field enhancement factor were extracted from the FE data using the orthodox Fowler–Nordheim theory. Folded CNT film cathodes mounted in the parallel alignment configuration produced the highest emission currents, while demonstrating a larger emission area and lower field enhancement factor.
ISSN:0021-8979
1089-7550
DOI:10.1063/5.0038937