Interaction of Microstructure and Interfacial Adhesion on Impact Performance of Polylactide (PLA) Ternary Blends

Polyactide (PLA) was blended with an ethylene/n-butyl acrylate/glycidyl methacrylate (EBA-GMA) terpolymer and a zinc ionomer of ethylene/methacrylic acid (EMAA-Zn) copolymer. The phase morphology of the resulting ternary blends and its relationship with impact behaviors were studied systematically....

Full description

Saved in:
Bibliographic Details
Published in:Macromolecules 2011-03, Vol.44 (6), p.1513-1522
Main Authors: Liu, Hongzhi, Song, Wenjia, Chen, Feng, Guo, Li, Zhang, Jinwen
Format: Article
Language:English
Subjects:
Applied sciences
Exact sciences and technology
Organic polymers
Physicochemistry of polymers
Properties and characterization
Structure, morphology and analysis
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Polyactide (PLA) was blended with an ethylene/n-butyl acrylate/glycidyl methacrylate (EBA-GMA) terpolymer and a zinc ionomer of ethylene/methacrylic acid (EMAA-Zn) copolymer. The phase morphology of the resulting ternary blends and its relationship with impact behaviors were studied systematically. Dynamic vulcanization of EBA-GMA in the presence of EMAA-Zn was investigated by torque rheology, and its cross-link level was evaluated by dynamic mechanical analysis. Reactive compatibilization between PLA and EBA-GMA was studied using Fourier transform infrared spectroscopy. The dispersed domains in the ternary blends displayed a “salami”-like phase structure, in which the EMAA-Zn phase evolved from occluded subinclusions into continuous phase with decrease in the EBA-GMA/EMAA-Zn ratio. An optimum range of particle sizes of the dispersed domains for high impact toughness was identified. Also, the micromechanical deformation process of these ternary blends was also investigated by observation of the impact-fractured surfaces using the electron microscope. It was suggested that the low cavitation resistance of dispersed particles in conjunction with suitable interfacial adhesion was responsible for the optimum impact toughness observed.