Luminescence of the Narrow-Band Red Emitting Nitridomagnesosilicate Li2(Ca1–x Sr x )2[Mg2Si2N6]:Eu2+ (x = 0–0.06)
The nitridomagnesosilicates Li2Ca2[Mg2Si2N6]:Eu2+ and Li2(Ca1.88Sr0.12)[Mg2Si2N6]:Eu2+ show narrow-band red emission at 638 and 634 nm, respectively, with an emission bandwidth of 62 nm (∼1513 cm–1) after excitation in the blue spectral region. Ce3+-doped samples show luminescence in the green spec...
Saved in:
Published in: | Chemistry of materials 2017-02, Vol.29 (3), p.1377-1383 |
---|---|
Main Authors: | , , , , |
Format: | Article |
Language: | English |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | The nitridomagnesosilicates Li2Ca2[Mg2Si2N6]:Eu2+ and Li2(Ca1.88Sr0.12)[Mg2Si2N6]:Eu2+ show narrow-band red emission at 638 and 634 nm, respectively, with an emission bandwidth of 62 nm (∼1513 cm–1) after excitation in the blue spectral region. Ce3+-doped samples show luminescence in the green spectral range (λem = 540 nm). The compounds were synthesized via solid-state metathesis reaction in Li melts. Refinement of single-crystal X-ray diffraction data revealed that Li2(Ca1.88Sr0.12)[Mg2Si2N6] crystallizes isomorphic to Li2Ca2[Mg2Si2N6]: C2/m [Z = 2, a = 5.5744(2), b = 9.8439(3), c = 6.0170(2) Å, β = 97.2520(10)°, R 1 = 0.021, wR 2 = 0.047]. Crystal composition was checked by EDS and ICP-OES measurements and luminescence properties are compared to state of the art narrow-band red emitting luminophors. On the basis of its narrow-band emission, application of the novel red luminophor in high CRI white pcLEDs is promising. |
---|---|
ISSN: | 0897-4756 1520-5002 |
DOI: | 10.1021/acs.chemmater.6b05196 |